EIS Evaluation of corrosion resistance of AISI 304 stainless steel exposed to Pseudomonas Stutzeri,
In this work, the formation of a Pseudomonas stutzeri biofilm in a marine medium on AISI 304 stainless steel was observed to evaluate the effects of biofilm formation on metallic passivation and corrosion processes. Open circuit potential and electrochemical impedance measurements were carried out...
Saved in:
| 主要作者: | |
|---|---|
| 其他作者: | , , , |
| 格式: | Artículo |
| 语言: | English |
| 出版: |
2021
|
| 主题: | |
| 在线阅读: | https://doi.org/10.20964/2021.05.39 http://www.electrochemsci.org/papers/vol16/21058.pdf |
| 标签: |
添加标签
没有标签, 成为第一个标记此记录!
|
| 总结: | In this work, the formation of a Pseudomonas stutzeri biofilm in a marine medium on AISI 304 stainless
steel was observed to evaluate the effects of biofilm formation on metallic passivation and corrosion
processes. Open circuit potential and electrochemical impedance measurements were carried out for 21
days on abiotic and biotic electrochemical cells. The influence of biofilm formation on corrosion
potential was monitored and used to propose a mechanism based on the impedance and corrosion
resistance values. In the abiotic cell, the corrosion resistance varied periodically, which was attributed
to the electrolytic activity of the medium on the metal. However, corrosion resistance increased in the
presence of bacteria and continued to increase as immersion time increased. Exopolymeric substances
were deposited onto the electrode, suggesting that P. stutzeri RPh9 colonized the metallic surface,
passivating the stainless steel electrode surface through continuous biofilm formation. Detachment of
the biofilm on day 21 was the likely cause of decreased corrosion resistance at the end of the experiment. |
|---|