Influence of γ phase on the magnetostructural transition and magnetocaloric properties in Ni38Co12Mn41Sn9 melt-spun ribbons
In the present work, Ni38Co12Mn41Sn9 melt-spun ribbons were annealed under different conditions to make samples free of secondary γ phase precipitates or get them with various average grain sizes. A comparative study was carried out to demonstrate how γ phase formation affects the martensitic transf...
Saved in:
| 其他作者: | , , , , , |
|---|---|
| 格式: | Artículo |
| 語言: | English |
| 出版: |
2023
|
| 主題: | |
| 在線閱讀: | https://doi.org/10.1016/j.jmmm.2023.170900 https://www.sciencedirect.com/science/article/abs/pii/S0304885323005504?via%3Dihub |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | In the present work, Ni38Co12Mn41Sn9 melt-spun ribbons were annealed under different conditions to make samples free of secondary γ phase precipitates or get them with various average grain sizes. A comparative study was carried out to demonstrate how γ phase formation affects the martensitic transformation (MT) and the magnetocaloric properties linked to the first-order phase transition. The γ phase significantly reduces the structural transformation temperatures, while slightly increases the thermal hysteresis. The γ phase also decreases the maximum entropy change (|ΔS|max) and the effect is more significant for smaller γ phase precipitates. As compared with those with coarse γ phase grains, the ribbons containing smaller ones possess a lower |ΔS|max but a smaller maximum magnetic hysteresis loss. |
|---|