Influence of γ phase on the magnetostructural transition and magnetocaloric properties in Ni38Co12Mn41Sn9 melt-spun ribbons
In the present work, Ni38Co12Mn41Sn9 melt-spun ribbons were annealed under different conditions to make samples free of secondary γ phase precipitates or get them with various average grain sizes. A comparative study was carried out to demonstrate how γ phase formation affects the martensitic transf...
Uloženo v:
| Další autoři: | , , , , , |
|---|---|
| Médium: | Artículo |
| Jazyk: | English |
| Vydáno: |
2023
|
| Témata: | |
| On-line přístup: | https://doi.org/10.1016/j.jmmm.2023.170900 https://www.sciencedirect.com/science/article/abs/pii/S0304885323005504?via%3Dihub |
| Tagy: |
Přidat tag
Žádné tagy, Buďte první, kdo otaguje tento záznam!
|
| Shrnutí: | In the present work, Ni38Co12Mn41Sn9 melt-spun ribbons were annealed under different conditions to make samples free of secondary γ phase precipitates or get them with various average grain sizes. A comparative study was carried out to demonstrate how γ phase formation affects the martensitic transformation (MT) and the magnetocaloric properties linked to the first-order phase transition. The γ phase significantly reduces the structural transformation temperatures, while slightly increases the thermal hysteresis. The γ phase also decreases the maximum entropy change (|ΔS|max) and the effect is more significant for smaller γ phase precipitates. As compared with those with coarse γ phase grains, the ribbons containing smaller ones possess a lower |ΔS|max but a smaller maximum magnetic hysteresis loss. |
|---|